Isitini se-silica refractory siyayiphikisa i-asidi futhi inokumelana nokuguguleka kwe-acid slag. I-Slica bricks refractoriness ngaphansi komthwalo ifika ku-1640 ~ 1690 ℃, izinga lokushisa elibonakalayo lokuqala lokuthambisa lingu-1620 ~ 1670 ℃ futhi ukuminyana kweqiniso ngu-2.35g/cm3. Isitini somlilo se-silicon singasebenza ngokushisa okuphezulu isikhathi eside futhi sigcine ukuqina kwevolumu ngaphandle kokuguqulwa. Isitini sokuvuselela i-silicon siqukethe okuqukethwe kwe-SiO2 okungaphezu kuka-94%. Isitini se-silicate sinamandla aphakeme okushisa aphezulu kanye nokumelana nokushaqeka okuphansi kokushisa. Isitini somlilo se-silicate senziwe nge-silica ore yemvelo njengempahla eluhlaza, yengeza i-mineralizer efanelekile ukukhuthaza i-quartz emzimbeni oluhlaza oguqulwa ube yi-tridymite futhi iqhunyiswe kancane ngezinga lokushisa elingu-1350 ~ 1430 ℃ ekwehliseni umkhathi. Lapho kushisa kufika ku-1450 ℃, kubalwa u-1.5 ~ 2.2% wesamba sokunwetshwa kwevolumu. Lokhu kwandiswa emva kokwandiswa kuzokwenza ukusika okuhlangene kuvalwe uphawu futhi kuqinisekise ukuthi ukwakhiwa kugcina umoya omuhle ongangenisi kanye namandla esakhiwo.
I-Silicon fire block iyisitena esiphikisayo ukuthi okuqukethwe kwe-silica kungaphezu kuka-93%, 50% -80% we-tridymite, 10% -30% wesigaba se-cristobalite, i-quartz nengilazi, cishe u-5% -15%. Ukwakheka kwe-mineralogical yezitini ze-silicate ikakhulukazi i-quartz ne-quartz, kanye nenani elincane le-quartz ne-vitreous. I-quartz yesikali, i-quartz ye-quartz kanye ne-quartz esele ishintsha kakhulu ngevolumu ngenxa yokushintsha kwesimo sekristalu ekushiseni okuphansi, ngakho-ke ukuzinza okushisayo kwesitini esiphikisayo se-silicate akubi kahle ekushiseni okuphansi. Enqubweni yokusebenzisa, ngaphansi kuka-800 ℃ ukunciphisa ukushisa nokupholisa, ukuze ugweme ukuqhekeka. Ngakho-ke akufanele kube ngaphansi kwezinga lokushisa elingu-800 ℃ kuhhavini.
Izitini zomlilo ze-silicate zenziwe nge-quartzite ngenani elincane le-agent ye-mineralizing. Lapho kushiswa ngezinga lokushisa eliphezulu, ukwakheka kwezitini ze-silica refractory amaminerali kwenziwa nge-quartz yesikali, i-quartzite quartz, ingilazi nezinye izicubu zesigaba eziyinkimbinkimbi ezakhiwe ekushiseni okuphezulu, futhi okuqukethwe kwe-AiO2 kungaphezu kwama-93%. Phakathi kwezitini ze-silica ezibaselwe kangcono, okuqukethwe kwe-quartz yesikali kuphakeme kakhulu, kubalwa ku-50% ~ 80%. cristobalit kwaba ngokulandelayo, ibalwa 10% kuphela 30%. Okuqukethwe kwesigaba se-quartz nengilazi kushintshashintsha phakathi kuka-5% no-15%
Into/Inkomba | QG-0.8 | QG-1.0 | QG-1.1 | QG-1.15 | QG-1.2 |
SiO2 % | ≥88 | ≥91 | ≥91 | ≥91 | ≥91 |
Ukuminyana ngobuningi g/cm3 | ≤0.85 | ≤1.00 | ≤1.10 | ≤1.15 | ≤1.20 |
Amandla Okuchotshozwa Okubandayo Mpa | ≥1.0 | ≥2.0 | ≥3.0 | ≥5.0 | ≥5.0 |
0.2Mpa Refractoriness Under Load T0.6℃ | ≥1400 | ≥1420 | ≥1460 | ≥1500 | ≥1520 |
Ushintsho Lomugqa Ongunaphakade Ekushisiseni Kabusha % 1450℃*2h | 0~+0.5 | 0~+0.5 | 0~+0.5 | 0~+0.5 | 0~+0.5 |
20~1000℃ Ukunwetshwa Kwezishisayo 10~6/℃ | 1.3 | 1.3 | 1.3 | 1.3 | 1.3 |
I-Thermal Conductivity (w/m*k) 350℃ | 0.55 | 0.55 | 0.6 | 0.65 | 0.7 |
Izitini zomlilo ze-silica zisetshenziswa kakhulu njengezinto eziphikisayo zodonga oluvikelayo lwegumbi lokubhaka kanye ne-combustor kuhhavini ye-coke, igumbi lokuvuselela kabusha kanye nephakethe le-slag esithandweni somlilo esivulekile sensimbi, isithando somgodi esicwiliswayo nesithando somlilo esincibilikisa ingilazi, kanye nezinye izindawo ezithwala isisindo nangaphezulu ku-ceramic. umlilo wokudubula. Izitini ze-silicate nazo zingasetshenziselwa indawo yokuthwala isisindo lapho izinga lokushisa eliphezulu liphezulu nangaphezulu kwesithando somlilo esivulekile esine-asidi.