I-Ultra-high Strength Nano Insulation Block
I-conductivity ephansi yokushisa
Amandla okushisa aphansi
Ukuzinza okuhle
Amandla aphezulu
Ukonga amandla
Thola Ukucaphuna Kwakamuva
Incazelo emfushane
Izinga lokushisa lohlangothi olubandayo lwama-onela amakhulu embonini kasimende ngokuvamile lingama-280-320℃. Njengoba kungekho lutho olunamandla amakhulu kanye ne-conductivity ephansi ye-thermal, ayikwazi ukufakwa ngokuphumelelayo, okuholela ekulahlekeni okukhulu kwamandla. Ngokwezibalo, ukusebenzisa i-40-50mm ewugqinsi we-ultra-high i-nano insulation block eneziko elivamile likasimende elisebenza ngongqimba kunganciphisa izinga lokushisa elibandayo lomzimba ka-100℃-130℃. Ulayini wokukhiqiza i-clinker wosayizi omaphakathi onamandla okukhiqiza nsuku zonke angamathani angu-5,000 ungonga cishe amathani angu-5,500 amalahle ajwayelekile ngonyaka. Ingonga ama-yuan ayizigidi eziyizinkulungwane ezingama-20 wezindleko zikaphethiloli njalo ngonyaka kuhhavini likasimende elijikelezayo. Ingasaphathwa-ke eyokuthi, kufakwe izinhlobo ezahlukene zeziko lokushisela ama-rotary ezimbonini eziningi, ezingonga amakhulu ezigidigidi zamabhizinisi minyaka yonke.
Izinzuzo
Lolu chungechunge lomkhiqizo luklanyelwe ukugcwalisa igebe lesicelo emakethe yendabuko.
Inamandla okuchoboza ezitini eziminyene ezinobuningi obungu-2.3g/cm3 kanye nokushiswa kwezitini ezikhanyayo ezinobuningi obungu-0.8g/cm3.
Iyindlela engcono kakhulu yokukhetha okokufaka kuhhavini lukasimende, ihhavini elijikelezayo lemfucuza eyingozi, i-alumina calcination rotary kiln, i-pellet rotary kiln namanye ama-oyela ashukumisayo anezidingo eziphezulu zamandla okuchoboza wezinto zokufakelwa.
Ukucaciswa
| Imikhiqizo | I-Ultra-high Strength Nano Insulation Brick RSNJ-1 | Ultra-hihg Amandla Nano Insulation Brick RSNJ-2 | LZ-65 High Alumina Brick | 0.8 I-Mullite Insulating Brick |
| RUL,0.2MPa×0.6% | ≥1580 | ≥1400 | ≥1500 | 0.05MPa×0.5% ≥1200 |
| BD, g/cm³ | ≤1.7 | ≤1.7 | ≥2.5 | ≤0.8 |
| I-CCS, i-MPa | ≥50 | ≥50 | ≥50 | ≥1.5 |
| I-PLC,% | 1500℃×12h -0.1-0.1 | 1400℃×12h -0.2-0.2 | 1450℃×12h -0.4-0.1 | 1350℃×12h -1.5-0.5 |
| TC,W/(mK) | I-Hot Side 800 ℃ | 0.399 | 0.600 | 1.5 | 0.35 |
| I-Hot Side 1100 ℃ | 0.411 | 0.650 | 1.6 | 0.40 |